HDPE TRB-115

Short Description:

Marlex Brand

HDPE| Film

Made In United States

Price: 1000-1200 USD/MT

Port: Huangpu / Ningbo / Shanghai / Qingdao

MOQ: 1*40GP

CAS No: 9002-88-4

HS Code: :3901200099

Payment: TT/ LC

Send email to us Download as PDF

Product Detail

Description

• Good bubble stability and film drawdown.
• High impact strength and toughness.
• Excellent stiffness and tensile strength.
• Balanced tear strength.

Applications

• T-shirt bags
• Produce bags
• Merchandise bags
• Industrial liners
• Trash can liners

Specifications

FDA 21 CFR 177.1520(c) 3.2a. The resin may be used in contact with all types of food as defined in Table 1, 21 CFR 176.170(c) and at use conditions B-H as defined in Table 2, 21 CFR 176.170(c).

Nominal Resin Properties	English	SI	Method
Melt Index, 190 °C/2.16 kg	-	0.06 g/10 min	ASTM D1238
HLMI, 190 °C/21.6 kg	-	9.5g/10 min	ASTM D1238
Density	-	0.950 g/cm³	ASTM D1505

Nominal Blown Film Properties at 0.5 mil¹	English	SI	Method
Dart	260 g/mil	100 N/mm	ASTM D1709
Elmendorf Tear MD	15 g/mil	6 N/mm	ASTM D1922
Elmendorf Tear TD	450 g/mil	174 N/mm	ASTM D1922
Tensile Strength at Break MD	13,000 psi	90 MPa	ASTM D882
Tensile Strength at Break TD	6,000 psi	41 MPa	ASTM D882
Tensile Elongation at Break MD	260 %	260 %	ASTM D882
Tensile Elongation at Break TD	570 %	570 %	ASTM D882
1 % Secant Modulus MD	120,000 psi	827 MPa	ASTM D882
1 % Secant Modulus TD	140,000 psi	965 MPa	ASTM D882

0.5 mil (12.7 micron) film produced using a grooved-feed extruder at a rate of 225 lb/h with a stalk height of 7 x Die Diameter, a 4:1 Blow-Up
Ratio (BUR), a 6 inch die diameter and a 0.040 inch die gap. The nominal properties reported herein are representative of the product under
these processing conditions, although film properties can vary depending on the specific film-blowing conditions. Therefore, the data should
not be used for specification purposes.